OEM manufacturer Hino Leaf Spring - Auto part truck spring leaf light duty truck leaf spring – Jiachuang Detail:
This spring assy are widely used in Russia for light duty truck .
Spring Measurements Specs
Totally 3 blades+2pcs plate ,1-2 blade Width(mm)*Thickness(mm): 60*8, the 3rd blade Width(mm)*Thickness(mm): 60*15 , 2pcs plate Width(mm)*Thickness(mm):60*8 . Eye to Eye Measurement 1200 mm (Free Length Measurement),Tolerance range within ±3mm . we also can provide bushings as long as customers advise the detailed dimensions.
Free Arch Measurement (see picture) 155mm,Tolerance range within ±5mm .
All datas are obtained by measuring the new produce product .
We have full range material stock:width 40mm-150mm,thickness 5mm-60mm,material grade SUP9, SUP11A , 55Cr3, SAE5160H , 50CrVA , 51CrV4 , 52CrMoV4 .
Our products high quality control by the advanced production line :automatic eye rolling machine , automatic queching machine,automatic parabolic machine .
We are in a good position not only to supply you high quality and competitive price , but also the excellent after sales service,Well-trained engineers will offer you any technical supports .
We got ISO9001 certification,our product acquired goods feedbacks from our customers .
Small trial orders can be accepted, sample is available.
We will provide the technical drawings to the customer to check all the details, We have a professional quality inspection section that will inspect each product before shipment and provide the inspection report to the customer . We also can help customers arrange all matters for the shipment delivery .
Key Points Keep The High Quality
| 1) Raw matrail . |
| Thickness less than 20mm. we choose SUP9/55Cr3/SAE5160H as the product material |
| Thickness from 20-30mm. wE choose SUP11A/50CrVA |
| Thickness more than 30mm. We choose 51CrV4 as the raw material |
| Thickness more than 50mm. We choose 52CrMoV4 as the raw material |
| 2) Quchenging Process |
| We strickly controled the steel temeprure around 800 degree. |
| we swing the spring in the qenching oil among 10 seconds according to the spring thickness. |
| 3)Shot Peening. |
| Each assmembing spring set under stress peening . |
| Fatigue test can reach over 150000 cycus |
| 4) Painting |
| Each leaf under cataphoresis painting. |
| Salt spray testing reach 500hours |
Production Process
1.Material Cutting
4.Edge Cutting
7.Stress Peening
2.Punching
5.Quenching
8.Assembling
3.Eye Rolling
6.Tempering
9.Painting
FAQ
Q1: What type of leaf spring could you produce ?
A: We can produce most kinds of springs in the market. especially on the parabolic springs.
Q2: What material could you supply for leaf spring?
A: Our material grade should be SUP9/SUP9A /SUP11A/51CrV4 /52CrMoV4/ even 55Cr3 and SAE5160H as well .
Q3: How long will be your delivery time?
A: 20-40days. If material stock enough around 20days. if not,would be 40days
Q4: What payment terms are acceptable?
A: TT and LC at sight
Q5: What is the packing?
A: No fumigation wooden pallet . we also can pack according to whatever you request if reasonable.
Q6:How about the surface finishing ?
A : electrophoresis coating (black,red,gray,or as customer’s requests )
Product detail pictures:
Related Product Guide:
The client satisfaction is our primary concentrate on. We uphold a consistent level of professionalism, top quality, credibility and service for OEM manufacturer Hino Leaf Spring - Auto part truck spring leaf light duty truck leaf spring – Jiachuang, The product will supply to all over the world, such as: Montreal, Ukraine, Rotterdam, Our company considers that selling is not only to gain profit but also popularize the culture of our company to the world. So we are working hard to give you the wholehearted service and willing to give you the most competitive price in the market
By Anna from Vietnam - 2017.11.01 17:04
We have been engaged in this industry for many years, we appreciate the work attitude and production capacity of the company, this is a reputable and professional manufacturer.
By Roberta from Costa Rica - 2017.05.02 18:28